Application

• Micares®X1087BK R11 is a flexible casting resin system based on polyurethane, consisting of resin and hardener. This two component potting compound designed for use in the electrical  engineering  and  the  electronics  is cold to thermal-curing. It is solvent free and liquid at ambient temperature (RT) .The resin component contains the filler and is degassed.

Processing

• It is easy to process at ambient temperature and atmospheric pressure.

Description

• Flexible, synthetic materials. The resin adheres well to metallic and non-metallic materials and resists tracking. Dielectric loss are low. The system is RoHS conform (European Directive 2002/95/EC). The system is UL 94V-0 listed.

Instructions

• The resin and hardener are mixed according to the specified ratio at ambient temperature, preferably using automatic dosing and mixing equipment. If the resin has been stored for a long period of time, it is recommended to stir well the complete content of the container and to check the viscosity before the processing is being started. Formation of lumps has to be prevented by applying of appropriate stirring conditions. The mixture is applied at ambient temperature (above 18℃)。The moulds should be treated with a release agent (e.g.MICAFIL 8055) to facilitate subsequent mould removal. For complicated components, or if optimal electrical properties are specified, casting under vacuum is required. Components and moulds generally do not need pre-heating for casting with Micares®X1087BK R11. Reactivity of the casting compound however, can be changed on request, and or by pre-heating the mould to about 40℃ to 80℃, e.g, to reduce cycle-time. Accelerator  can   be   used   without   adverse effects on the final properties of the resin. We can supply a suitable product separately.

Curing/post-curing

• This resin is especially designed for hardening at ambient temperature . The curing time depends on the resin quantity and temperature. Final curing  therefore can be achieved after a few hours or days. Or considerably less at higher temperatures. The self-heating effect of low  exothermal  reaction  in  the  resin, depending on the resin quantity, is usually sufficient to bring it to final hardness in 10-24 hours.

Storage

• Polyols and isocyanate based hardeners can be stored for one year in the original sealed tin s stored in a cool, dry place. The hardeners may present an increase in viscosity that does not change the cured system properties. Both components should be stored in appropriate room  in  their  originally  sealed  containers. Avoid storage outside! The resin is chemically stable. However, before use, the resin must be carefully  stirred  with  a  suitable  equipment since all resins containing mineral filler tend to build deposits. Stirring with particular care is necessary, when the resin has been stored for a long period of time. Important: the hardener must be kept away from any exposure to humidity. It should always be stored well sealed.

Health & Safety

• Refer to Elantas Zhuhai Material Safety Data Sheet (MSDS) .

Shelf life

• 12 months (in unopened containers stored below 25°C).