2. Low Temperature Cure Resin System:
a. PRL-213 SERIES:
 Feature: Higher temperature service requirement, designed for structural applications with higher thermal resistance and gives excellent wet-out of fiberglass, carbon and aramid fibers.
 Curing Condition: 80℃~150℃
 Suitable Process: Wet layup / RTM 

b. PRL-0428 SERIES:
 Feature: Low curing temperature, and low curing pressure; suitable for large and/or thick-walled curing parts.
 Curing Condition: 75℃~120℃
 Suitable Process: Autoclave / Press moulding / VBO available

3. Medium Temperature Cure Resin System:
a. PRM-TOUT SERIES:
 Feature: Toughened epoxy systems. This series is toughened and controlled flow epoxy matrixes designed for outer pressure processes, featuring:
1. Good impact strength
2. Remarkable fatigue resistance 
3. Less fiber misalignment appearance resistance
 Curing Condition: 130℃~150℃
 Suitable Process: SW/bladder moulding / Press moulding

b. PRM-IP SERIES:
 Feature: Toughened epoxy systems. This series is toughened and controlled flow epoxy matrixes designed for inner pressure processes, featuring:
1. Good impact strength
2. Remarkable fatigue resistance
 Curing Condition: 130℃~150℃
 Suitable Process: Bladder moulding / Press moulding

c. PRM-622 SERIES:
 Feature: With no change of curing parameters under current medium temperature (at 150℃) curing process, this series can impart a shiny and transparent skin to the cured products as well as no 'white spot' after sanding with water. Excellent for woven fabrics.
 Curing Condition: 125℃~150℃

d. PRM-HTG351 SERIES:
 Feature: Toughened epoxy systems; god hot performance.
 Curing Condition: 125℃~150℃
 Suitable Process: Press moulding / Bladder moulding / Autoclave
4. High Temperature Cure Resin System:
a. PRH-HTG434 SERIES:
 Feature: Toughened epoxy system, good hot performance
 Curing Condition: 180℃
 Suitable Process: SW moulding / Autoclave / Press moulding

b. PRH-HTGII SERIES:
 Feature: Toughened epoxy system, good hot performance
 Curing Condition: 180℃
 Suitable Process: Autoclave / Press moulding

c. PRH-MB5M1P SERIES
 Feature: Toughened BMI system; for the requirement of high temperature service above 200℃. In application where the cured composites parts are lightly loaded, short period exposure above 250℃ can be sustained.
 Curing Condition: 180℃
 Suitable Process: Autoclave / Press moulding



5. Rapid Cure Resin System:
a. PRM-D1-R SERIES:
 Feature: 
1. Toughened epoxy resin
2. High cycle moulding process
3. 150℃/3 minutes or 130℃/10 minutes. 
4. High temperature demoulding available (Hot-in-Hot-out).
 Curing Condition: 120℃~150℃
 Suitable Process: Vacuum bag / Autoclave / Press moulding

b. PRM-D2-R SERIES:
 Feature: 
1. Toughened epoxy resin
2. High cycle moulding process
3. 150℃/3 minutes or 130℃/10 minutes. 
4. High temperature demoulding available (Hot-in-Hot-out).
5. For both the application of prepreg of longfiber and sheet molding compound.
 Curing Condition: 120℃~150℃
 Suitable Process: Vacuum bag / Autoclave / Press moulding


6. Flame Retardant Resin System:
a. PRM-D1-RF SERIES:
 Feature: 
1. UL94(V0)
2. FAR 25.853(FST)
3. Rapid cure at 150℃/10 minutes.
4. High temperature demoulding avaliable (Hot-in-Hot-out).
 Curing Condition: 150℃
 Suitable Process: Press moulding

b. PRM-MTC2-RF SERIES:
 Feature: 
1. FAR 25.853(FST+HRR)
2. Designed to meet FST and HRR requirements for aircraft cabin interiors.
 Curing Condition: 135℃~150℃
 Suitable Process: Press moulding

c. PRH-HTG-RF:
 Feature: 
1. FAR 25.853(FST+HRR)
2. Flame retardant epoxy system with above 150℃ service capabilities.
 Curing Condition: 180℃
 Suitable Process: Press moulding